DuPont™ Zytel®
nylon resin
Product guide and properties
® Registered trademarks of E.I. du Pont de Nemours and Company
The miracles of science™ is a trademark of E.I. du Pont de Nemours and Company
1 2
4
3
16
12
10
8
6
4
2
0
2 4 6 8 10 12 14
Stiffness2)
To
ug
hn
es
s1
)
Glass reinforced ZYTEL®
Toughened glass reinforced ZYTEL®
Toughened ZYTEL®
ST801
14 490
408
450
114
42 101
151 135
79G13
80G14
80G25
80G33
70G20
70G25
70G30
70G43
70G35 70G503)
Toughness-Stiffness Ratio of various ZYTEL® resins compared to ZYTEL® 101L
2
Photographs
1 – Residual circuit breaker – glass-mineral reinforced
2 – Air intake manifold – glass reinforced
3 – Sole for cycling shoes – glass reinforced
4 – Flat filter housing – glass reinforced
5 – Resonator – glass reinforced
6 – Hedge-trimmer housing – glass reinforced
5
6
1) Notched Izod impact, DAM 2) Flexural modulus, 50% RH 3) Preliminary data
Introduction
ZYTEL® is DuPont’s registered trademark for its com-
prehensive range of nylon resins. Since the invention
of nylon by DuPont in the 1930s, it has become the
most widely used of all engineering polymers. Due to
their excellent balance of properties, nylon components
(produced by injection moulding, extrusion or blow
moulding) find extensive use in many applications
including: automotive, electrical/electronic, domestic
appliances, furniture and construction.
Products and properties
ZYTEL® nylon resins are classified by chemical compo-
siton into the following groups:
– Nylon 66
– Nylon 6
– Nylon 66/6 blends
– Nylon 612
– Transparent amorphous nylon
– Semi-aromatic High Temperature Nylon.
The key features of ZYTEL® nylons are:
– High mechanical strength
– Excellent balance of stiffness/toughness
– Good high temperature performance
– Good electrical and flammability properties
– Good abrasion and chemical resistance.
Properties such as melting point, moisture absorption
and modulus of elasticity are primarily determined by
the type of nylon.
In addition, nylons can be readily modified and rein-
forced, to create a wide range of products with tailored
properties for specific processes and end-uses.
Major “families” of ZYTEL® nylons described in this
brochure include:
– Unreinforced
– Tough/Supertough
– Glass reinforced
– Toughened/glass reinforced
– Flame retardant
– High viscosity/Extrusion
– Speciality
– High performance polyamide resin.
Only standard compositions are described in this
brochure.
DuPont™ Zytel®
nylon resin
3
Properties of ZYTEL® HTN resins are given in the bro-
chure “ZYTEL® HTN – Product guide and properties”.
Mineral and mineral/glass reinforced nylons are also
available under the MINLON® trademark. Information
on these products is given in the brochure “MINLON® –
Product guide and properties”.
Data
All data in this brochure is taken from Campus version
4.0 (measured according to ISO standards), except
where otherwise specified. In addition, all data is for
natural colour material except where otherwise speci-
fied.
Physical description
ZYTEL® nylon resins are solid granular materials,
typically cylinder cut with nominal dimensions of
3 × 2,5 mm. Most compositions are available in
colours, either cube blended or fully compounded.
Packaging
ZYTEL® nylon resins are available in 4 standard
packaging types:
– 40 × 25 kg bags
– 1000 kg octabin
– 1000 kg octabin (with bottom unloading)
– Bulk shipments.
Full details of these packaging types are given in the
brochures: “Introduction to Engineering Polymers
Packaging Materials” and “Silo Shipments”.
Processing
ZYTEL® nylon resins are supplied in moisture proof
packaging, so that drying should not normally be nec-
essary. However, nylon resins are hygroscopic and
absorb moisture on exposure to the atmosphere.
If excessive moisture absorption has occurred, then the
resin must be dried at 80°C to less than 0,2% moisture
content before processing.
These products can be processed on conventional
injection moulding, blow moulding or extrusion equip-
ment, depending on the grade selected. Detailed rec-
ommendations for processing ZYTEL® nylon resins can
be obtained from DuPont sales and distributor offices
listed on the back of this brochure.
MINLON® is a registered trademark of E.I. du Pont de Nemours and Company
4
Compositions
** Certain NC’s are available in lubricated and non-heat stabilised.
Designation Description
Unreinforced p. 6
ZYTEL® 101L Lubricated PA66
ZYTEL® 101F Fast moulding PA66
ZYTEL® 103HSL Heat stabilised lubricated PA66
ZYTEL® 103FHS Fast moulding heat stabilised PA66
ZYTEL® 105F Lubricated UV resistant PA66 (Black)
ZYTEL® EFE1068 Slightly nucleated PA66
ZYTEL® 135F Nucleated lubricated PA66
ZYTEL® 7335F Nucleated lubricated PA6
ZYTEL® 151L Lubricated PA612
ZYTEL® 153HSL Heat stabilised lubricated PA612
Toughened p. 9
ZYTEL® 114L BK097 Impact modified PA66 (Black)
ZYTEL® 408 Toughened PA66
ZYTEL® 450 Toughened PA66
ZYTEL® 490 Toughened PA66
ZYTEL® 7300T Toughened PA6
ZYTEL® 7331T Toughened PA6
Supertough p. 10
ZYTEL® ST801 Supertough PA66
ZYTEL® ST7301 Supertough PA6
Specialities p. 11
ZYTEL® FN718 PA66 based flexible nylon alloy
ZYTEL® FN727 PA6 based flexible nylon alloy
ZYTEL® ST811HS Toughened PA6 extrusion grade, heat stabilised
Glass reinforced* p. 11
ZYTEL® 70G20HSL 20% glass reinforced heat stabilised and lubricated PA66
ZYTEL® 70G25HSL 25% glass reinforced heat stabilised PA66
ZYTEL® 70G30HSL 30% glass reinforced heat stabilised PA66
ZYTEL® 70G35HSL 35% glass reinforced heat stabilised PA66
ZYTEL® 70G43HSL 43% glass reinforced heat stabilised PA66
ZYTEL® 70G50HSL 50% glass reinforced heat stabilised PA66
ZYTEL® 73G15L/HSL 15% glass reinforced PA6
ZYTEL® 73G20L 20% glass reinforced PA6
ZYTEL® 73G30L/HSL 30% glass reinforced PA6
ZYTEL® 73G35L/HSL 35% glass reinforced PA6
ZYTEL® 73G45L/HSL 45% glass reinforced PA6
Hydrolysis resistant, glass reinforced p. 15
ZYTEL® 70G25HSLR 25% glass reinforced, hydrolysis resistant PA66, heat stabilised and lubricated
ZYTEL® 70G30HSLR 30% glass reinforced, hydrolysis resistant PA66, heat stabilised and lubricated
ZYTEL® 70G30HSR2 30% glass reinforced, ultra-high hydrolysis resistant PA66, heat stabilised and lubricated
5
Compositions
Designation Description
Glass reinforced (Speciality) p. 16
ZYTEL® 70G33GRA Glass reinforced lubricated PA66
ZYTEL® 70G35HSLX 35% glass reinforced hot oil and grease resistant PA66
ZYTEL® 70G35HSLRA4 Easy flow glass reinforced PA66
ZYTEL® 70GB40HSL 40% glass bead reinforced heat stabilised PA66
ZYTEL® 74G33EHSL 33% glass reinforced heat stabilised PA66/6 blend
ZYTEL® 74G33EL 33% glass reinforced PA66/6 blend
ZYTEL® 77G33L 33% glass reinforced PA612
ZYTEL® 70K20HSL 20% KEVLAR® reinforced PA66
Toughened glass reinforced p. 18
ZYTEL® 79G13L Toughened 13% glass reinforced PA66
ZYTEL® 80G14 Toughened 14% glass reinforced PA66
ZYTEL® 80G25 Toughened 25% glass reinforced PA66
ZYTEL® 80G33HS1L Toughened 33% glass reinforced heat stabilised PA66
ZYTEL® 73G30T Toughened 30% glass reinforced PA6
Flame retardant p. 20
ZYTEL® FR7026V0F Unreinforced PA66 polymer, UL94 V0 (0,5 mm)
ZYTEL® FR72G25V0 25% glass reinforced PA66/6 copolymer, UL94 V0 (0,5 mm)
ZYTEL® FR70G25GW 25% glass reinforced glow wire 850°C PA66 at 1 mm
ZYTEL® FR70G25V0 25% glass reinforced PA66, UL94 V0 (0,5 mm)
ZYTEL® FR70M30V0 30% mineral reinforced PA66, UL94 V0 (1,6 mm)
ZYTEL® FR70M40GW 40% mineral reinforced glow wire 960°C PA66 at 1,5 mm
High viscosity/Extrusion p. 22
ZYTEL® E40 High viscosity PA66 (VN = 180-150)
ZYTEL® E42A High viscosity PA66 (VN = 225-325)
ZYTEL® E51HSB High viscosity heat stabilised PA66 (VN = 272-352)
ZYTEL® 158 High viscosity PA612
Unreinforced
PA66 PA66
Test ZYTEL® 101L ZYTEL® 101F
Property conditions Standard ISO Units DAM 50% RH DAM 50% RH
Yield stress 50 mm/min, 23°C 527-1/-2 MPa 83 53 83 53
Yield strain 50 mm/min, 23°C 527-1/-2 % 4,5 25 4,5 25
Stress at break (tensile) 5 mm/min, 23°C 527-1/-2 MPa
Strain at break (tensile) 5 mm/min, 23°C 527-1/-2 %
50 mm/min, 23°C 40 >50 40 >50
Nominal strain at break 50 mm/min, 23°C 527-1/-2 % 22 >100 18 >100
Tensile modulus 1 mm/min, 23°C 527-1/-2 MPa 3100 1200 3100 1200
Charpy impact strength (unnotched) 23°C 179/1eU kJ/m2 NB NB NB NB
–30°C NB NB NB NB
Charpy impact strength (notched) 23°C 179/1eA kJ/m2 5 15 5 15
–30°C 4 4 4 4
Izod impact strength (notched) 23°C 180/1A kJ/m2 5 13 5 13
–30°C 5 4 5 4
Melting temperature 10°C/min 11357-1/-3 °C 263 263
Temperature of deflection under load 0,45 MPa 75-1/-2 °C 200 200
1,8 MPa 70 70
Vicat softening temperature 50N, 50°C/h 306 °C 240 240
Coefficient of linear thermal expansion
Parallel (in flow direction) 23°C-55°C 11359-2 10 –4/°C 1 1
Normal (perpendicular to flow) 23°C-55°C 1,1 1,1
Comparative tracking index 23°C IEC 60112 V 600 600
Electric strength (dielectric strength) 1 mm, 23°C IEC 60243-1 kV/mm 31 28 31 26
Surface resistivity 23°C IEC 60093 ohm 1012 >1015 1012 1012
Volume resistivity 23°C IEC 60093 ohm · m 1012 1010 1014 1011
Relative permittivity 102 Hz, 1 mm, 23°C IEC 60250 3,8 10,9 3,8 10,9
106 Hz, 1 mm, 23°C 3,5 4 3,5 4,6
Dissipation factor 102 Hz, 1 mm, 23°C IEC 60250 10–4 80 2100 140 2100
106 Hz, 1 mm, 23°C 180 750 180 1000
Density 1183 kg/m3 1140 1140
Flammability classification1) 1,5 mm UL 94/ISO1210 V2 V2
Glow wire flammability index 1,5 mm 60695-2-1 °C 850 850
Oxygen index 4589-1-2 % 28 31 28
Water absorption Equilibrium, 50% RH, 23°C Similar % 2,7 2,7
Saturation, immersed, 23°C to ISO 62 8,5 8,5
Rockwell hardness Scale M, 23°C 2039/2 79 59 71
Scale R, 23°C 121 108 113
Ball indentation hardness H 358/30 23°C 2039-1 MPa 85
H 961/30 23°C 160
Mould shrinkage2) Parallel (in flow direction) 2 mm 294-4 % 1,3 1,3
Normal (perpendicular to flow) 2 mm 1,3 1,3
6
Properties of ZYTEL® nylon resins
M
EC
HA
N
IC
AL
TH
ER
M
AL
EL
EC
TR
IC
AL
OT
HE
RS
1) Numerical flame test ratings are not intended to present behaviour of moulded parts in real life fire conditions; each end-user must determine whether any potential flammability hazards exist with parts moulded from ZYTEL® nylon
resins. UL yellow cards available upon request.
2) Depends on moulding conditions.
All the above information is subject to the disclaimer printed on the back page of this document.
7
All the above information is subject to the disclaimer printed on the back page of this document.
Unreinforced
PA66 PA66 PA66 PA66 PA66 PA6
ZYTEL® 103HSL ZYTEL® 103FHS ZYTEL® 105F ZYTEL® EFE1068 ZYTEL® 135F ZYTEL® 7335F
DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH
85 54 85 54 85 60 85 59 98 69 90 55
4,4 25 4,4 25 25 4,5 25 4,5 18 4 24
40 >50 35 >50 30 >50 35 >60 18 >50 30 >50
20 >100 20 >100 24 >50 18 >60 13 >50 8 >50
3100 1250 3100 1250 3200 1500 3100 1500 3600 2100 4000 1400
NB NB NB NB 45 NB NB NB NB NB 40 NB
NB NB NB NB 55 55 NB NB 110 60
5 14 5 14 6 15 6 13 4 9 4 18
4 4 4 4 4 3 3 3 2 3
5 14 5 14 5 12 5 11 3 6,5 3 1,5
6 5 5 4 3 2,3 2 2 1,5
263 263 263 263 263 223
200 200 205 210 185
70 70 70 70 90 70
240 240 240 245 200
1 1 1 0,85 1,21 0,76
1,1 1,1 1,1 0,82 1,21 0,92
525 600 600
31 28 25
1012 1012 1015 1013
1013 1010 1013 1010 1013
3,8 13 3,9 8,7 4,2
3,5 4 3,6 4,6 3,8 3,9
75 5800 70 2400 300
165 700 300 600 200 600
1140 1140 1140 1140 1140 1130
V2 V2 V2 V2 V2 HB
950 950 850
28 28 27
2,7 2,7 2,7 2,8 2,7 3
8,5 8,5 8,5 8,5 8,5 9
87 64
121 121 121 123 116
1,3 1,5 0,8 0,5
1,3 1,3 0,5
8
Unreinforced
PA612 PA612
Test ZYTEL® 151L ZYTEL® 153HSL
Property conditions Standard ISO Units DAM 50% RH DAM 50% RH
Yield stress 50 mm/min, 23°C 527-1/-2 MPa 62 54 62 53
Yield strain 50 mm/min, 23°C 527-1/-2 % 4,5 18 4,4 19
Stress at break (tensile) 5 mm/min, 23°C 527-1/-2 MPa
Strain at break (tensile) 5 mm/min, 23°C 527-1/-2 %
50 mm/min, 23°C 100 >100
Nominal strain at break 50 mm/min, 23°C 527-1/-2 % 17 >50 30 >50
Tensile modulus 1 mm/min, 23°C 527-1/-2 MPa 2400 1700 2400 1600
Charpy impact strength (unnotched) 23°C 179/1eU kJ/m2 NB NB NB NB
–30°C NB 40 NB NB
Charpy impact strength (notched) 23°C 179/1eA kJ/m2 3,5 4 4 7
–30°C 3,5 3 5 4
Izod impact strength (notched) 23°C 180/1A kJ/m2 4 4,5 4 6
–30°C 4,5 3 5 5
Melting temperature 10°C/min 11357-1/-3 °C 218 218
Temperature of deflection under load 0,45 MPa 75-1/-2 °C 135 135
1,8 MPa 62 62
Vicat softening temperature 50N, 50°C/h 306 °C 181 181
Coefficient of linear thermal expansion
Parallel (in flow direction) 23°C-55°C 11359-2 10 –4/°C 1,1 1,2
Normal (perpendicular to flow) 23°C-55°C 1,2 1,2
Comparative tracking index 23°C IEC 60112 V
Electric strength (dielectric strength) 1 mm, 23°C IEC 60243-1 kV/mm
Surface resistivity 23°C IEC 60093 ohm 1012 1012 1012
Volume resistivity 23°C IEC 60093 ohm · m 1013 1011 1013 1011
Relative permittivity 102 Hz, 1 mm, 23°C IEC 60250 3,6 5 3,6 5,3
106 Hz, 1 mm, 23°C 3,2 4 3,2 3,4
Dissipation factor 102 Hz, 1 mm, 23°C IEC 60250 10–4 135 700 140 1000
106 Hz, 1 mm, 23°C 160 400 160 400
Density 1183 kg/m3 1060 1060
Flammability classification1) 1,5 mm UL 94/ISO1210 V2 HB
Glow wire flammability index 1,5 mm 60695-2-1 °C 675
Oxygen index 4589-1-2 % 27 27
Water absorption Equilibrium, 50% RH, 23°C Similar % 1,3 1,3
Saturation, immersed, 23°C to ISO 62 3 3
Rockwell hardness Scale M, 23°C 2039/2
Scale R, 23°C 114 103 114
Ball indentation hardness H 358/30 23°C 2039-1 MPa
H 961/30 23°C
Mould shrinkage2) Parallel (in flow direction) 2 mm 294-4 % 1,2 1,2
Normal (perpendicular to flow) 2 mm 1,2 1,2
Properties of ZYTEL® nylon resins
M
EC
HA
N
IC
AL
TH
ER
M
AL
EL
EC
TR
IC
AL
OT
HE
RS
1) Numerical flame test ratings are not intended to present behaviour of moulded parts in real life fire conditions; each end-user must determine whether any potential flammability hazards exist with parts moulded from ZYTEL® nylon
resins. UL yellow cards available upon request.
2) Depends on moulding conditions.
All the above information is subject to the disclaimer printed on the back page of this document.
9
All the above information is subject to the disclaimer printed on the back page of this document.
Toughened
PA66 PA66 PA66 PA66 PA6 PA6
ZYTEL® 114L BK097 ZYTEL® 408 ZYTEL® 450 ZYTEL® 490 ZYTEL® 7300T ZYTEL® 7331T
DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH
75 52 61 43 55 40 55 40 68 40 62 39
7 25 6 26 5,4 29 5,5 29 4 30 4,4 26
30 >100 55 >100 50 >100 50 >100 40 >100 86 >100
20 >50 35 >50 28 >50 33 >50 15 >50 49 >50
3000 1400 2200 1100 2200 1000 2100 950 2750 890 2630 970
NB NB NB NB NB NB NB NB NB NB NB NB
NB NB NB NB NB NB NB NB NB NB
12 20 18 25 18 50 67 104 14 110 16 30
8 5 15 6 10 9 20 15 9 5 10 6
10 15 19 20 17 70 66 83 11 90 16 32
7 5 11 4 10 8 17 16 13 6 10 5
263 263 263 263 223 223
150 155 92 85 75 194
75 65 65 70 55 55
225 210 195 220 195
1,21 1,32 1,61 1,52 1,04
1,21 1,32 1,61 1,52 1,22
575 600 600 600
33,5
1015 1015
1012 1011 1013 1011 1013 1010
3,7 6,6 3,2 7
3,2 3,6 2,9 3,7
200 1500
200 600 200 500
1120 1090 1080 1080 1100 1090
HB HB HB HB HB
675
19
2,5 2,2 2,2 2,3 2,6
7,9 7 7 7,1 9
76 71 50
118 115 102
85
123
1,1 1,2 1,7 1,6 0,6
1,2 0,9 1,3 1,1 0,7 1
10
Supertough
PA66 PA6
Test ZYTEL® ST801 ZYTEL® ST7301
Property conditions Standard ISO Units DAM 50% RH DAM 50% RH
Yield stress 50 mm/min, 23°C 527-1/-2 MPa 50 43 48 30
Yield strain 50 mm/min, 23°C 527-1/-2 % 5,7 37 4 32
Stress at break (tensile) 5 mm/min, 23°C 527-1/-2 MPa
Strain at break (tensile) 5 mm/min, 23°C 527-1/-2 %
50 mm/min, 23°C 60 >100 90 >200
Nominal strain at break 50 mm/min, 23°C 527-1/-2 % 40 >50 >30 >200
Tensile modulus 1 mm/min, 23°C 527-1/-2 MPa 2000 900 1900 660
Charpy impact strength (unnotched) 23°C 179/1eU kJ/m2 NB NB NB NB
–30°C NB NB NB NB
Charpy impact strength (notched) 23°C 179/1eA kJ/m2 80 115 80 125
–30°C 18 17 19 18
Izod impact strength (notched) 23°C 180/1A kJ/m2 80 94 60 90
–30°C 20 20
Melting temperature 10°C/min 11357-1/-3 °C 263 223
Temperature of deflection under load 0,45 MPa 75-1/-2 °C 130 75
1,8 MPa 65 50
Vicat softening temperature 50N, 50°C/h 306 °C 205
Coefficient of linear thermal expansion
Parallel (in flow direction) 23°C-55°C 11359-2 10 –4/°C 1,2
Normal (perpendicular to flow) 23°C-55°C 0,9
Comparative tracking index 23°C IEC 60112 V 600
Electric strength (dielectric strength) 1 mm, 23°C IEC 60243-1 kV/mm 31 39
Surface resistivity 23°C IEC 60093 ohm 1015 1015
Volume resistivity 23°C IEC 60093 ohm · m 1012 1011
Relative permittivity 102 Hz, 1 mm, 23°C IEC 60250 3,2 8
106 Hz, 1 mm, 23°C 2,9 3,6
Dissipation factor 102 Hz, 1 mm, 23°C IEC 60250 10–4 80 1800
106 Hz, 1 mm, 23°C 140 550
Density 1183 kg/m3 1080 1060
Flammability classification1) 1,5 mm UL 94/ISO1210 HB HB
Glow wire flammability index 1,5 mm 60695-2-1 °C 675
Oxygen index 4589-1-2 % 20
Water absorption Equilibrium, 50% RH, 23°C Similar % 2,2
Saturation, immersed, 23°C to ISO 62 6,7
Rockwell hardness Scale M, 23°C 2039/2
Scale R, 23°C 112 89
Ball indentation hardness H 358/30 23°C 2039-1 MPa
H 961/30 23°C
Mould shrinkage2) Parallel (in flow direction) 2 mm 294-4 % 1,6
Normal (perpendicular to flow) 2 mm 1 1,3
Properties of ZYTEL® nylon resins
M
EC
HA
N
IC
AL
TH
ER
M
AL
EL
EC
TR
IC
AL
OT
HE
RS
1) Numerical flame test ratings are not intended to present behaviour of moulded parts in real life fire conditions; each end-user must determine whether any potential flammability hazards exist with parts moulded from ZYTEL® nylon
resins. UL yellow cards available upon request.
2) Depends on moulding conditions.
All the above information is subject to the disclaimer printed on the back page of this document.
All the above information is subject to the disclaimer printed on the back page of this document.
11
Specialities Glass reinforced
PA66 PA6 PA6 PA66 PA66
ZYTEL® FN718 ZYTEL® FN727 ZYTEL® ST811HS ZYTEL® 70G20HSL ZYTEL® 70G25HSL
DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH DAM 50% RH
30 23 25 31
50 >50 44 >50 4
>50 >50 >50 >50 159 103 180 115
2,9 7 3,1 5
130
>50 >50 >50 >50
960 420 770 350 900 400 7300 5000 8600 6100
NB NB NB NB 55 75 65 85
NB NB NB NB 50 45 53 47
125 130 71 129 9 9,5 10 12
35 65 14 13 9 9 10 11
NB NB NB NB 8 9 10 11
NB NB 7 7 8 8
263 223 218 263 263
170 260 263
50 45 47 250 250
220 180 95 255 255
1,2 1,2 1,2 2 0,35 0,33
1,8 1,11 1,12
400 400
>1015 1012 1015 1013
>1013 109 1013 109
3,9 4,4 4,1 4,5
160 700 150 730
1040 1020 1040 1290 1330
HB HB HB HB
2,3 2,1 2
6,8 6,8 6,4
57 102 85 103 87
70 122 115 123 116
250 155 252 164
1,4 1,8 0,45 0,4
1,3 1,1 1,1
12
Glass reinforced
PA66 PA66
Test ZYTEL® 70G30HSL ZYTEL® 70G35HSL
Property conditions Standard ISO Units DAM 50% RH DAM 50% RH
Yield stress 50 mm/min, 23°C 527-1/-2 MPa
Yield strain 50 mm/min, 23°C 527-1/-2 %
Stress at break (tensile) 5 mm/min, 23°C 527-1/-2 MPa 200 140 215 150
Strain at break (tensile) 5 mm/min, 23°C 527-1/-2 % 3,4 5 3,2 4,6
50 mm/min, 23°C 3 5
Nominal strain at break 50 mm/min, 23°C 527-1/-2 %
Tensile modulus 1 mm/min, 23°C 527-1/-2 MPa 10000 7200 11200 8300
Charpy impact strength (unnotched) 23°C 179/1eU kJ/m2 82 95 95 100
–30°C 80 73 88 75
Charpy impact strength (notched) 23°C 179/1eA kJ/m2 14 15 15 17
–30°C 10 10 10 10
Izod impact strength (notched) 23°C 180/1A kJ/m2 13 17 12 15
–30°C 12 10 10 10
Melting temperature 10°C/min 11357-1/-3 °C 263 263
Temperature of deflection under load 0,45 MPa 75-1/-2 °C 260 260, 261
1,8 MPa 250 250
Vicat softening temperature 50N, 50°C/h 306 °C 250 255
Coefficient of linear thermal expansion
Parallel (in flow direction) 23°C-55°C 11359-2 10 –4/°C 0,22 0,2
Normal (perpendicular to flow) 23°C-55°C 1,07 1
Comparative tracking index 23°C IEC 60112 V 400 400
Electric strength (dielectric strength) 1 mm, 23°C IEC 60243-1 kV/mm 38 32
Surface resistivity 23°C IEC 60093 ohm >1015 1013 >1015 1013
Volume resistivity 23°C IEC 60093 ohm · m >1013 109 1013 109
Relative permittivity 102 Hz, 1 mm, 23°C IEC 60250 4,4 10,8
106 Hz, 1 mm, 23°C 4,1 4,6 4,1 4,7
Dissipation factor 102 Hz, 1 mm, 23°C IEC 60250 10–4 70 4600
106 Hz, 1 mm, 23°C 150 650 140 620
Density 1183 kg/m3 1370 1410
Flammabi
本文档为【ZYTPPe 杜邦尼龙材料】,请使用软件OFFICE或WPS软件打开。作品中的文字与图均可以修改和编辑,
图片更改请在作品中右键图片并更换,文字修改请直接点击文字进行修改,也可以新增和删除文档中的内容。
该文档来自用户分享,如有侵权行为请发邮件ishare@vip.sina.com联系网站客服,我们会及时删除。
[版权声明] 本站所有资料为用户分享产生,若发现您的权利被侵害,请联系客服邮件isharekefu@iask.cn,我们尽快处理。
本作品所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用。
网站提供的党政主题相关内容(国旗、国徽、党徽..)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。