Technical data sheet for VINNAPAS® C 305 / Version: 1.1 / Date of last alteration: 16.09.2010 1 / 2
Product description
VINNAPAS® C 305 is a solid, colorless to pale
yellowish copolymer of vinyl acetate and crotonic acid.
Properties
VINNAPAS® C 305 is a physically drying,
thermoplastic binder which forms films through solvent
evaporation. When appropriate solvents are used, the
dry films are odorless.
Application
Typical applications for VINNAPAS® C 305:
- moisture-sensitive adhesives
- finishes for the textile and hat industries
- inks for fabrics, leather. Marks made with such inks
can easily be removed with slightly alkaline water.
- lacquers removable by aqueous alkali, often in
combination with hard resins.
- hairspray
Processing
Product data
Melt viscosity, 100% Polymer
Bohlin high temperature viscosimeter
100 °C ~ 7000 Pa·s
120 °C ~ 2000 Pa·s
140 °C ~ 300 Pa·s
160 °C ~ 80 Pa·s
Solvents
VINNAPAS® C 305 is soluble in esters, ketones and
methanol. Solutions in 94% ethyl alcohol are turbid,
but the films deposited from them are almost clear
when dry. The resin is only partly soluble in toluene.
Solutions with solids contents of up to 50% can be
made with good solvents such as acetone and ethyl
acetate.
VINNAPAS® C 305 will dissolve in alkaline water,
although this is a time-consuming operation resulting
in high viscosity solutions. Solution may be speeded
up by also using a water soluble solvent and using the
following formulation as a guide:
40 parts VINNAPAS® C 305
35 parts water
10 parts conc. Ammonia
30 parts methanol
Acetone may be used instead of methanol. The
solution can be diluted by stirring in more water. An
alternative method consists of dissolving the resin only
in acetone and then diluting the resultant solution with
water containing ammonia.
Care should be taken not to exceed a pH value of 8
since otherwise, the resin will be partly saponified and
the solution will gel. Dilute caustic potash and certain
organic amines can also be used instead of ammonia.
Sodium and calcium hydroxide are unsuitable for this
purpose since insoluble salts are formed with sodium
and calcium ions.
Plasticizers
VINNAPAS® C 305 may be plasticized with the
plasticizers normally used for polyvinyl acetate, e. g.
dibutyl phthalate and tricresyl phosphate.
Resins
VINNAPAS® C 305 is readily compatible with
VINNAPAS® B 100 and VINNAPAS® UW 10, Phenolic
Resin BKR 2620, Synthetic Resin SK and AP,
Phthalopal PP, Epikote 1001 as well as low to high
viscosity nitrocellulose, with all of which it may be
blended. Compatibility with Plexigum MB 319,
Staybelite Ester 5, Rocramar NN, Alkydal F 25 and
Laroplal S is but limited. It is always advisable to
check compatibility by lab tests in advance.
Storage
To prevent caking VINNAPAS® C 305 should not be
stored at temperatures above 20°C. Storage
conditions must be dry; material must be protected
from direct sun exposure.
Under these conditions the product has a shelf life of
at least 12 months.
Packaging
VINNAPAS® C 305 is supplied in 25 kg Paper Bags.
Big Bag is available on request.
VINNAPAS® C 305
VINYL ACETATE COPOLYMER, CAS NO. 25609-89-6
Technical data sheet for VINNAPAS® C 305 / Version: 1.1 / Date of last alteration: 16.09.2010 2 / 2
Additional information
If VINNAPAS® C 305 is used in applications other than
those mentioned, the choice, processing and use of
VINNAPAS® C 305 is the sole responsibility of the
purchaser. All legal and other regulations must be
complied with.
Further information is available upon request.
Safety notes
Comprehensive instructions are given in the
corresponding Material Safety Data Sheets. They are
available on request from WACKER subsidiaries or
may be printed via WACKER web site
http://www.wacker.com.
Product data
Specification data Inspection Method Value
20 Acid number specific method 30 - 38 mg KOH/g
10 Viscosity (10% in ethyl acetate), 20 °C ASTM D 445 - 06 2,5 - 3,5 mPa*s
Typical general characteristics Inspection Method Value
40 Efflux time DIN2431 4M approx. 26 s
70 Softening point DIN ISO 4625,
by Ring and Ball
approx. 95 °C
50 Density of the polymer DIN EN ISO 1183 /1-3 approx. 1,18 g/cm³
30 Volatiles specific method < 0,5 wt. %
45 Supply form solid, colorless to pale
yellowish flakes
60 K-value DIN 53726 29 - 33
80 Molecular weight (MW) SEC, PS-Standard approx. 45000 g/mol
90 Glass transition temperature DSC
DIN EN ISO 11357-2
approx. 47 °C
These figures are only intended as a guide and should not be used in preparing specifications.
The data presented in this leaflet are in accordance with the present state of
our knowledge, but do not absolve the user from carefully checking all
supplies immediately on receipt. We reserve the right to alter product
constants within the scope of technical progress or new developments. The
recommendations made in this leaflet should be checked by preliminary trials
because of conditions during processing over which we have no control,
especially where other companies' raw materials are also being used. The
recommendations do not absolve the user from the obligation of investigating
the possibility of infringement of third parties' rights and, if necessary,
clarifying the position. Recommendations for use do not constitute a warranty,
either express or implied, of the fitness or suitability of the products for a
particular purpose.
The management system has been
certified according to DIN EN ISO
9001 and DIN EN ISO 14001
WACKER is a trademark of Wacker
Chemie AG.
VINNAPAS® is a trademark of
Wacker Chemie AG.
For technical, quality, or product
safety questions, please contact:
Wacker Chemie AG
Hanns-Seidel-Platz 4
81737 München, Germany
info.polymers@wacker.com
www.wacker.com
本文档为【聚乙酸乙烯酯 VINNAPAS C 305】,请使用软件OFFICE或WPS软件打开。作品中的文字与图均可以修改和编辑,
图片更改请在作品中右键图片并更换,文字修改请直接点击文字进行修改,也可以新增和删除文档中的内容。
该文档来自用户分享,如有侵权行为请发邮件ishare@vip.sina.com联系网站客服,我们会及时删除。
[版权声明] 本站所有资料为用户分享产生,若发现您的权利被侵害,请联系客服邮件isharekefu@iask.cn,我们尽快处理。
本作品所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用。
网站提供的党政主题相关内容(国旗、国徽、党徽..)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。