树枝状分子作为附着力促进剂的优势和良好性能树枝状分子作为附着力促进剂的优势和良好性能
传统的有机附着力促进剂存在制备困难、易导致金属盖层区域有缺陷、附着力不可再生等缺点,利用胺封端的G8 PAMAM树枝状大分子作为气相沉积金薄膜和硅基衬底之间的附着力促进剂,制备方法比较简单,只需将基板清洗,浸渍和漂洗,而且重现性好和电化学稳定,容易实现大范围的应用。威海晨源化工新材料有限公司整理自《Dendrimer-Mediated Adhesion between Vapor-Deposited Au and Glass or Si Wafers》Lane A. ...
树枝状分子作为附着力促进剂的优势和良好性能
传统的有机附着力促进剂存在制备困难、易导致金属盖层区域有缺陷、附着力不可再生等缺点,利用胺封端的G8 PAMAM树枝状大分子作为气相沉积金薄膜和硅基衬底之间的附着力促进剂,制备方法比较简单,只需将基板清洗,浸渍和漂洗,而且重现性好和电化学稳定,容易实现大范围的应用。威海晨源化工新材料有限公司整理自《Dendrimer-Mediated Adhesion between Vapor-Deposited Au and Glass or Si Wafers》Lane A. Baker, Francis P. Zamborini, Li Sun, and Richard M. Crooks Department of Chemistry, Texas A&M University Anal. Chem. 1999, 71, 4403-4406
Dendrimer's advantages and good performance used as adhesion promoter.
The traditional organic adhesion promoter presents difficult preparation, easy to cause defect of the metal overlayer ,non-renewable adhesion and other shortcomings, using amine-terminated
G8 PAMAM dendrimers as adhesion promoters between vapor-deposited gold thin film and the silicon substrate, preparation method is simple, only clean ,dip and rinse the substrate, and with good reproducibility, and electrochemically stability, easy to achieve wide range applications. Weihai CY Dendrimer Technology Co. Ltd. forwards from “Dendrimer-Mediated Adhesion between Vapor-Deposited Au and Glass or Si Wafers” Lane A. Baker, Francis P. Zamborini, Li Sun, and Richard M. Crooks Department of Chemistry, Texas A&M University Anal. Chem. 1999, 71, 4403-4406
本文档为【树枝状分子作为附着力促进剂的优势和良好性能】，请使用软件OFFICE或WPS软件打开。作品中的文字与图均可以修改和编辑，
图片更改请在作品中右键图片并更换，文字修改请直接点击文字进行修改，也可以新增和删除文档中的内容。
该文档来自用户分享，如有侵权行为请发邮件ishare@vip.sina.com联系网站客服，我们会及时删除。
[版权声明] 本站所有资料为用户分享产生，若发现您的权利被侵害，请联系客服邮件isharekefu@iask.cn，我们尽快处理。
本作品所展示的图片、画像、字体、音乐的版权可能需版权方额外授权，请谨慎使用。
网站提供的党政主题相关内容(国旗、国徽、党徽..)目的在于配合国家政策宣传，仅限个人学习分享使用，禁止用于任何广告和商用目的。
浙公网安备 33021202002483