制订Made by:
审核Verified by:
批准Approved by:
焊接工艺规程
Pre-Welding procedure specification(pWPS)
No.: pWPS-WTI-0801
日期 Date:
地点: 评定或检验机构:
Location: Examiner or test body:
工艺编号:pWPS-WTI-0801 工艺评定编号:
Welding procedure reference No.: WPAR No. :
制造商: 焊工姓名:
Manufacturer: Welder,s name:
焊接方法:气体保护焊 135 焊接位置:平焊
Welding process: MAG 135 Welding positions:PA
接头类型:对接接头 坡口制备和清理方法:机械加工或气割 清磨
Joint type: butt joint Method of preparation and cleaning:
母材牌号及证书: Q690 母材厚度/规格(mm):12
Parent material specification: Material thickness/outside diameter(mm):12
焊材类别和牌号:实芯焊丝 ER 50-6 焊材特殊烘干规定:
Filler metal classification and trade name: Special baking or drying:
焊接准备情况(简图)*: 钨极种类/直径(mm):
Weld preparation details(Sketch)*: Tungsten electrode type/size:
焊接接头形式 Joint design 焊接顺序 Welding sequences
单位【Unit】:mm
焊接工艺参数:
Welding details:
焊道
Run
焊接方法
Process
焊材规格
Size of filler
metal (mm)
电流强度
Current
(A)
电弧电压
Voltage
(V)
电流种类/极性
Type of current
/Polarity
送丝速度
Wire feed
speed(㎜/s)
焊接速度*
Travel speed
(cm/min)
热输入*
Heat input
(KJ/mm)
1 MAG Φ1.2 140~150 20~21 DC/反接 14~16
2 MAG Φ1.2 200~220 21~24 Electrode positive 23~25
3 MAG Φ1.2 220~230 24~25 21~23
4 MAG Φ1.2 250~260 27~28 21~23
电弧保护
Shielding Ar80%+CO220%
电弧保护
Shielding 20 保护气体/焊剂
Gas/Flux 根部保护
Backing
气体流量
Gas flow rate
(L/min) 根部保护
Backing
衬垫保护情况: 清根情况:反面碳弧气刨清根
Details of backing: Details of back gouging:
预热温度:50~75℃ 层间温度: ≤200℃
Preheat temperature: Interpass temperature:
焊后热处理:消除应力退火 加热和冷却速度*:
Post-weld heat treatment: Heating and cooling rates*:
其它说明*
Other information*
焊丝干伸长度: 15~20mm 摆动(焊道最大宽度)(mm):
Contact tube-to-workpiece distance: Weaving(maximum width of run) (mm):
脉冲焊接情况: 离子焊接情况:
Pulse welding details: Plasma welding details:
制订Made by:
审核Verified by:
批准Approved by:
焊接工艺规程
Welding procedure specification(WPS)
No.: WPS-WTI-0810 日期 Date:
地点: 评定或检验机构:
Location: Examiner or test body:
工艺编号:WPS-WTI-0710 工艺评定编号:
Welding procedure reference No.: WPAR No. :
制造商: 焊工姓名:
Manufacturer: Welder,s name:
焊接方法:气体保护焊 135 焊接位置:平角焊
Welding process: MAG 135 Welding positions:PB
接头类型:T 型接头 坡口制备和清理方法:机械加工或气割 清磨
Joint type:T- joint(double bevel groove) Method of preparation and cleaning:
母材牌号及证书: Q690 母材厚度/规格(mm):20
Parent material specification: Material thickness/outside diameter(mm):20
焊材类别和牌号:实芯焊丝 ER 50-6 焊材特殊烘干规定:
Filler metal classification and trade name: Special baking or drying:
焊接准备情况(简图)*: 钨极种类/直径(mm):
Weld preparation details(Sketch)*: Tungsten electrode type/size:
焊接接头形式 Joint design 焊接顺序 Welding sequences
50°
±
5°
50
°
±
5°
7
610 8
11 9
5 3
4
2
焊接工艺参数:
Welding details:
焊道
Run
焊接方法
Process
焊材规格
Size of filler
metal (mm)
电流强度
Current
(A)
电弧电压
Voltage
(V)
电流种类/极性
Type of current
/Polarity
送丝速度
Wire feed
speed(㎜/s)
焊接速度*
Travel speed
(cm/min)
热输入*
Heat input
(KJ/mm)
1 封底 MAG Φ1.2 160~170 20~21 DC/反接 14~16
2 反面 MAG Φ1.2 220~230 23~24 Electrode positive 21~23
3~9 MAG Φ1.2 260~270 28~30 22~24
10~ MAG Φ1.2 280~290 30~31 22~24
电弧保护
Shielding Ar80%+CO220%
电弧保护
Shielding 20 保护气体/焊剂
Gas/Flux 根部保护
Backing
气体流量
Gas flow rate
(L/min) 根部保护
Backing
衬垫保护情况: 清根情况:反面碳弧气刨清根
Details of backing: Details of back gouging:
预热温度:100℃ 层间温度: ≤200℃
Preheat temperature: Interpass temperature:
焊后热处理: 加热和冷却速度*:
Post-weld heat treatment: Heating and cooling rates*:
其它说明*
Other information*
焊丝干伸长度: 15~20mm 摆动(焊道最大宽度)(mm):
Contact tube-to-workpiece distance: Weaving(maximum width of run) (mm):
脉冲焊接情况: 离子焊接情况:
Pulse welding details: Plasma welding details:
本文档为【WPS(新格式)HRY011】,请使用软件OFFICE或WPS软件打开。作品中的文字与图均可以修改和编辑,
图片更改请在作品中右键图片并更换,文字修改请直接点击文字进行修改,也可以新增和删除文档中的内容。
该文档来自用户分享,如有侵权行为请发邮件ishare@vip.sina.com联系网站客服,我们会及时删除。
[版权声明] 本站所有资料为用户分享产生,若发现您的权利被侵害,请联系客服邮件isharekefu@iask.cn,我们尽快处理。
本作品所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用。
网站提供的党政主题相关内容(国旗、国徽、党徽..)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。