Designation: A 572/A 572M – 04 American Association StateHighway and Transportation
Officals Standard
AASHTO No.: M223
Standard Specification for
High-Strength Low-Alloy Columbium-Vanadium Structural
Steel1
This standard is issued under the fixed designation A 572/A 572M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers five grades of high-strength
low-alloy structural steel shapes, plates, sheet piling, and bars.
Grades 42 [290], 50 [345], and 55 [380] are intended for
riveted, bolted, or welded structures. Grades 60 [415] and 65
[450] are intended for riveted or bolted construction of bridges,
or for riveted, bolted, or welded construction in other applica-
tions.
1.2 For applications, such as welded bridge construction,
where notch toughness is important, notch toughness require-
ments are to be negotiated between the purchaser and the
producer.
1.3 The use of columbium, vanadium, titanium, nitrogen, or
combinations thereof, within the limitations noted in Section 5,
is required; the selection of type (1, 2, 3, 4, or 5) is at the option
of the producer, unless otherwise specified by the purchaser.
(See Supplementary Requirement S90.)
1.4 The maximum thicknesses available in the grades and
products covered by this specification are shown in Table 1.
1.5 When the steel is to be welded, a welding procedure
suitable for the grade of steel and intended use or service is to
be utilized. See Appendix X3 of Specification A 6/A 6M for
information on weldability.
1.6 The values stated in either inch-pound units or SI units
are to be regarded separately as standard. Within the text, the
SI units are shown in brackets. The values stated in each
system are not exact equivalents; therefore, each system is to
be used independently of the other, without combining values
in any way.
1.7 The text of this specification contains notes or footnotes,
or both, that provide explanatory material. Such notes and
footnotes, excluding those in tables and figures, do not contain
any mandatory requirements.
1.8 For structural products produced from coil and fur-
nished without heat treatment or with stress relieving only, the
additional requirements, including additional testing require-
ments and the reporting of additional tests, of A 6/A 6M apply.
2. Referenced Documents
2.1 ASTM Standards: 2
A 6/A 6M Specification for General Requirements for
Rolled Structural Steel Bars, Plates, Shapes, and Sheet
Piling
A 36/A 36M Specification for Carbon Structural Steel
A 514/A 514M Specification for High-Yield Strength,
Quenched and Tempered Alloy Steel Plate, Suitable for
Welding
3. General Requirements for Delivery
3.1 Structural products furnished under this specification
shall conform to the requirements of the current edition of
Specification A 6/A 6M, for the specific structural product
ordered, unless a conflict exists in which case this specification
shall prevail.
3.2 Coils are excluded from qualification to this specifica-
tion until they are processed into a finished structural product.
Structural products produced from coil means structural prod-
ucts that have been cut to individual lengths from a coil. The
processor directly controls, or is responsible for, the operations
involved in the processing of a coil into a finished structural
product. Such operations include decoiling, leveling or
straightening, hot-forming or cold-forming (if applicable),
cutting to length, testing, inspection, conditioning, heat treat-
ment (if applicable), packaging, marking, loading for shipment,
and certification.
NOTE 1—For structural products produced from coil and furnished
without heat treatment or with stress relieving only, two test results are to
be reported for each qualifying coil. Additional requirements regarding
structural products produced from coil are described in A 6/A 6M.
1 This specification is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys, and is the direct responsibility of Subcommittee
A01.02 on Structural Steel for Bridges, Buildings, Rolling Stock, and Ships.
Current edition approved April 1, 2004. Published May 2004. Originally
approved in 1966. Last previous edition approved in 2003 as A 572/
A 572M – 03ae1.
2 For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website.
1
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
4. Materials and Manufacture
4.1 The steel shall be semi-killed or killed
5. Chemical Composition
5.1 The heat analysis shall conform to the requirements
prescribed in Table 2 and Table 3.
5.2 The steel shall conform on product analysis to the
requirements prescribed in Table 2 and Table 3, subject to the
product analysis tolerances in Specification A 6/A 6M.
6. Mechanical Properties
6.1 Tensile Properties:
6.1.1 The material as represented by the test specimens shall
conform to the tensile properties given in Table 4.
7. Keywords
7.1 bars; bolted construction; bridges; buildings;
columbium-vanadium; high-strength; low-alloy; plates; riveted
construction; shapes; sheet piling; steel; structural steel;
welded construction
TABLE 1 Maximum Product Thickness or Size
Grade
Yield Point, min Maximum Thickness or Size
Zees and Rolled
Teesksi [MPa]
Plates and Bars
Structural Shape
Flange or Leg
Thickness Sheet Piling
in. [mm] in. [mm]
42 [290]A 42 [290] 6 [150] all all all all
50 [345]A 50 [345] 4B [100]B all all all all
55 [380] 55 [380] 2 [50] all all all all
60 [415]A 60 [415] 11⁄4C [32]C 2 [50] all all
65 [450] 65 [450] 11⁄4 [32] 2 [50] not available all
A In the above tabulation, Grades 42, 50, and 60 [290, 345, and 415], are the yield point levels most closely approximating a geometric progression pattern between
36 ksi [250 MPa], min, yield point steels covered by Specification A 36/A 36M and 100 ksi [690 MPa], min, yield strength steels covered by Specification A 514/A 514M.
B Round bars up to and including 11 in. [275 mm] in diameter are permitted.
C Round bars up to and including 31⁄2 in. [90 mm] in diameter are permitted.
TABLE 2 Chemical RequirementsA
(Heat Analysis)
Diameter, Thickness,
or Distance
Between Parallel
Faces, in. [mm]
Plates and Bars
Structural
Shape
Flange or
Leg
Thickness,
in. [mm]
Grade Carbon,
max, %
Manganese,B
max, %
Phosphorus,
max, %
Sulfur,
max,
%
Silicon
Plates to 11⁄2 in. [40
mm] Thick,
Shapes with
Flange or Leg
Thickness to 3 in.
[75 mm] inclusive,
Sheet Piling,
Bars, Zees, and
Rolled TeesC
Plates Over 11⁄2 in.
[40 mm] Thick and
Shapes with Flange
Thickness
Over 3 in.
[75 mm]
max, % range, %
6 [150] all 42 [290] 0.21 1.35D 0.04 0.05 0.40 0.15–0.40
4 [100]E all 50 [345] 0.23 1.35D 0.04 0.05 0.40 0.15–0.40
2 [50]F all 55 [380] 0.25 1.35D 0.04 0.05 0.40 0.15-0.40
11⁄4 [32]F #2 [50] 60 [415] 0.26 1.35D 0.04 0.05 0.40 G
>1⁄2 – 11⁄4 [13–32] >1-2 [25-50] 65 [450] 0.23 1.65 0.04 0.05 0.40 G
#1⁄2 [13]H # 1H 65 [450] 0.26 1.35 0.04 0.05 0.40 G
A Copper when specified shall have a minimum content of 0.20 % by heat analysis (0.18 % by product analysis).
B Manganese, minimum, by heat analysis of 0.80 % (0.75 % by product analysis) shall be required for all plates over 3⁄8 in. [10 mm] in thickness; a minimum of 0.50 %
(0.45 % by product analysis) shall be required for plates 3⁄8 in. [10 mm] and less in thickness, and for all other products. The manganese to carbon ratio shall not be less
than 2 to 1.
C Bars over 11⁄2 in. [40 mm] in diameter, thickness, or distance between parallel faces shall be made by a killed steel practice.
D For each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximum
is permitted, up to a maximum of 1.50 %.
E Round bars up to and including 11 in. [275 mm] in diameter are permitted.
F Round bars up to and including 31⁄2 in. [90 mm] in diameter are permitted.
G The size and grade is not described in this specification.
H An alternative chemical requirement with a maximum carbon of 0.21 % and a maximum manganese of 1.65 % is permitted, with the balance of the elements as shown
in Table 2.
A 572/A 572M – 04
2
TABLE 3 Alloy Content
TypeA Elements HeatAnalysis, %
1 ColumbiumB 0.005–0.05C
2 Vanadium 0.01–0.15
3 ColumbiumB
Vanadium
Columbium plus vanadium
0.005-0.05C
0.01–0.15
0.02–0.15D
5 Titanium
Nitrogen
Vanadium
0.006-0.04
0.003–0.015
0.06 max
A Alloy content shall be in accordance with Type 1, 2, 3, or 5 and the contents
of the applicable elements shall be reported on the test report.
B Columbium shall be restricted to the following thicknesses and sizes unless
killed steel is furnished. Killed steel shall be confirmed by a statement of killed steel
on the test report, or by a report on the presence of a sufficient quantity of a strong
deoxidizing element, such as silicon at 0.10 % or higher, or aluminum at 0.015 %
or higher. See table below.
C Product analysis limits = 0.004 to 0.06 %.
D Product analysis limits = 0.01 to 0.16 %.
Grades
Maximum Plate, Bar,
Sheet
Piling, Zees, and Rolled
Tee Thicknesses, in. [mm]
Maximum Structural
Shape Flange or Leg
Thickness,
in. [mm]
42, 50, and 55 3⁄4 1.5
[290, 345, and
380]
[20] [40]
60 and 65 1⁄2 1
[415 and 450] [13] [25]
TABLE 4 Tensile RequirementsA
Grade
Yield Point, min Tensile Strength, min Minimum Elonga-tion, % B,C,D
ksi [MPa] ksi [MPa] in 8 in.[200 mm]
in 2 in.
[50 mm]
42 [290] 42 [290] 60 [415] 20 24
50 [345] 50 [345] 65 [450] 18 21
55 [380] 55 [380] 70 [485] 17 20
60 [415] 60 [415] 75 [520] 16 18
65 [450] 65 [450] 80 [550] 15 17
A See specimen Orientation under the Tension Tests section of Specification
A 6/A 6M.
B Elongation not required to be determined for floor plate.
C For wide flange shapes over 426 lb/ft [634 kg/m], elongation in 2 in. [50 mm]
of 19 % minimum applies.
D For plates wider than 24 in. [600 mm], the elongation requirement is reduced
two percentage points for Grades 42, 50, and 55 [290, 345, and 380], and three
percentage points for Grades 60 and 65 [415 and 450]. See elongation require-
ment adjustments in the Tension Tests section of Specification A 6/A 6M.
A 572/A 572M – 04
3
SUPPLEMENTARY REQUIREMENTS
Supplementary requirements shall not apply unless specified in the order or contract. Standardized
supplementary requirements for use at the option of the purchaser are listed in Specification A 6/A 6M.
Those that are considered suitable for use with this specification are listed by title:
S5. Charpy V-Notch Impact Test.
S18. Maximum Tensile Strength
S30. Charpy V-Notch Impact Test for Structural Shapes: Alternate Core Location
S32. Single Heat Bundles.
In addition, the following supplementary requirements are suitable for use:
S81. Tensile Strength
S81.1 For Grade 50 [345] steel of thicknesses 3⁄4 in. [20
mm] and less, the tensile strength shall be a minimum of 70 ksi
[485 MPa].
S90. Type
S90.1 The specific type of steel shall be as specified by the
purchaser in the order or contract.
SUMMARY OF CHANGES
Committee A01 has identified the location of selected changes to this standard since the last issue (A 572/A
572M-03e1) that may impact the use of this standard. (Approved April 1, 2004.)
(1) Supplementary Requirement S32 has been added. (2) Table 3 has been revised to remove Type 4.
Committee A01 has identified the location of selected changes to this standard since the last issue (A 572/A 572M-03) that
may impact the use of this standard. (Approved May 10, 2003.)
(1) Tables 1, 2, and 3 have been revised.
Committee A01 has identified the location of selected changes to this standard since the last issue (A 572/A 572M-02) that
may impact the use of this standard.
(1) 1.8, 3.1, 3.1.1 (renumbered as 3.2), and Note 1 have been
revised to be consistent with the terminology and requirements
of Specification A 6/A 6M.
(2) Table 1, footnote C was changed to 11 in. [275 mm].
(3) Table 2, footnote F was changed to 11 in. [275 mm].
ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.
This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org).
A 572/A 572M – 04
4
本文档为【A572标准】,请使用软件OFFICE或WPS软件打开。作品中的文字与图均可以修改和编辑,
图片更改请在作品中右键图片并更换,文字修改请直接点击文字进行修改,也可以新增和删除文档中的内容。
该文档来自用户分享,如有侵权行为请发邮件ishare@vip.sina.com联系网站客服,我们会及时删除。
[版权声明] 本站所有资料为用户分享产生,若发现您的权利被侵害,请联系客服邮件isharekefu@iask.cn,我们尽快处理。
本作品所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用。
网站提供的党政主题相关内容(国旗、国徽、党徽..)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。