江西涤纶厂直纺差别化涤纶长丝项目开工 合成纤维工业2004年第27卷 3结论 a.用多聚磷酸处理PBO纤维能够提高其与 树脂间的界面粘结强度,A溶液处理1min,可提 高24%,B溶液处理5min可提高55%左右.但 同时,纤维本身的强度有一定的下降.采用B溶 液处理PBO纤维比A溶液能够达到更好的改性 效果. b.A溶液处理1min后的纤维表面脱落,芯 层出现少量原纤维化.B溶液处理5min后纤维 表面有部分皮层溶胀脱落,表面并没有太大变化. c.处理后的PBO纤维接触角明显减小,表明 纤维表面亲水性大大提高,即纤维表面润湿性能 提高.处理后的PBO纤维结晶度轻微降低,对纤 维结晶结构没有太大的破坏. 参考文献 l刘新东,邱哲明,王斌等.PBO纤维表面分析与表面偶联剂处 理[J].固体火箭技术,2002,25(2):70—73 2RosenbergS,Quarderer,GeorgeJ,eta1.Methodforrapidspan- ningofapolybenzazolefiber[P].US,US5294390,1994 3SoYH,FroelieherSW,KaliszewskiB,eta1.StudyofPoly (benzo[1,2-d:5,4-dprime]bisoxazole-2,6-diyl-l,4-phenyle he)ReactionsatElevatedTemperatures[J].Macmmolecules, 1999,32(20):6565,6569 4SoYH,HeeschenJP.BellB.eta1.StudyoftheMechanismfor Poly(p-phenylene)benzoxazolePolymerization.aremarkableRe- actionPathwaytoMakeRigid-rodPolymers[J].Macmmolecules, 1998,31(16):5229,5239 5SoYH,SenA,KimP,eta1.MolecularCompositeFibersfrom RigidROdPolymersandThermosetResinMatrixes[J].PolymSci A:PolymChem,1995,33(17):2893,2899 6SOYH,HeeschenJP,BellB,eta1.Poly(P—phenylenebenzo- bisoxazole)FiberwithPolyphenyleneSulfidePendentGroups[J]. PolymSciA:PolymChem,1995,33(1):159,164 7SoYH,Mre’tinSJ.OwenK.eta1.StudyofBenzobisoxazoleand BenzobisthiazoleCompoundsandPolymersUnderHydrolyticCoil- ditions[J].JPolymPartA:PolymChem.1999,37(14): 2637,2643 8金士九,史卫华,王霞等.单丝拔出实验研究芳纶.环氧树脂界 面相[J].复合材料学报,1994,11(4):22,25 9王宜,胡健,张英东等.液滴形状法测量纤维接触角的研究 [J].合成纤维工业,2004.27(2):12—14 l0周贵恩,吴平平.聚亚苯基苯并二噻唑的X射线衍射研究 [J].高分子学报,1990,(5):520—525 11KitagawaT,KazuyukiY.ArelationshipBetweentheStressDistri- butionandthePeakProfileBroadeningofMeridionalX-RayDif- fractionfromPBOFiber[J].JouralofPolymerScience:PartB: PolymerPhysics,2000,38(22):2937,2942 SurfacemodificationofPBOfiberbypolyphosphoricacidtreatment LuoGuo,WangYi,HuJian,ZhengChisong,ZhouXuesong (StateKeyLaboratoryofPl咖 andPaperEngineering,SouthChinaUniversityofTechnology,Guangzhou510641) Abstract:Thesurfacemodificationofpolybenzazole(PBO)fiberwasconductedbyusingabuiltsolution ofpolyphosphoric acid(PPA)andalcoholatthevolumeratioof1:1.Theinterfacialadhesionbetweenfiberandresinswascha racterizedby measuringsingle—strandpull—outforce.ThehydrophilicityofPBOfiberwasevaluatedbydropletshapemethod.Thechangeof surfacemorphologyandcrystallinestructurewerediscussedbeforeandaftermodificationbySEMand X—raydiffractometry.The resultsshowedthattheadhesionbetweenfiberandresinswasincreasedby24%and55%,thesingle—stra ndstrengthwasre— duced,thecontactanglebetweenfiberanddropletwasdecreasedfromabove90.tonearly45.,andthecrys tallinitywasde— creasedfrom56.4%to52.9%and52.3%whenthePBOfiberwastreatedwithtwokindsofsolutionfor1mi nand5min.re. spectively. Keywords:polybenzazolefiber;polyphosphoricacid;alcohol;surfacemodification;chemicaltreatme nt;crystallinity ..I国内外动态 上海石化股份有限公司 扩建12kt/a涤纶工业丝 题述项目于2004年7月正式开工,这是已被 列入国家重点技术改造的”双高一优”项目,主要 包括2条普通丝生产线,2条高模低缩丝生产线 和1套15kt/a的固相聚合装置.该项目关键工 艺设备从日本东丽公司引进,其余设备全部国产 化.该项目 计划 项目进度计划表范例计划下载计划下载计划下载课程教学计划下载 在2004年年底试车投产. 江西涤纶厂直纺差别化涤纶长丝项目开工 据悉,江西涤纶厂180kt/a聚酯熔体直纺差 别化涤纶长丝项目已在南昌县小蓝工业园开工建 设,计划3年内建成投产.目前该厂的主导产品 为涤纶长丝,加工丝和坯绸,产品差别化率达 40%.具有涤纶长丝规模50kt/a,差别化涤纶长 丝产品以多孔细旦DTY为主,产量近150kt/a,涤 纶坯绸3km/a.(编委王德诚)