International Alloy Designations
and
Chemical Composition Limits
for
Wrought Aluminum and
Wrought Aluminum Alloys
The Aluminum Association
Incorporated
1525 Wilson Boulevard, Arlington, VA 22209
www.aluminum.org
With Support for On-line Access From:
Aluminum Extruders Council
Aluminium Federation of South Africa
Australian Aluminium Council Ltd.
European Aluminium Association
Japan Aluminium Association
S.C. Alprom S.A, Romania
Revised: April 2006
Supersedes: April 2004
© Copyright 2006, The Aluminum Association, Inc.
Unauthorized reproduction and sale by photocopy or any other method is illegal.
Use of the Information
The Aluminum Association has used its best efforts in compiling the information contained in this
publication. Although the Association believes that its compilation procedures are reliable, it does not
warrant, either expressly or impliedly, the accuracy or completeness of this information. The
Aluminum Association assumes no responsibility or liability for the use of the information herein.
All Aluminum Association published standards, data, specifications and other material are reviewed at
least every five years and revised, reaffirmed or withdrawn. Users are advised to contact The
Aluminum Association to ascertain whether the information in this publication has been superseded in
the interim between publication and proposed use.
CONTENTS
Page
FOREWORD ........................................................................................................... i
SIGNATORIES TO THE DECLARATION OF ACCORD ..................................... ii-iii
REGISTERED DESIGNATIONS AND CHEMICAL COMPOSITION LIMITS .... 1-12
Footnotes ................................................................................................... 13-14
TABLE OF NOMINAL DENSITIES FOR ACTIVE ALLOYS ............................. 15-19
TABLE OF INACTIVE ALLOY DESIGNATIONS ............................................. 20-21
Table of Chemical Composition Limits for Inactive Original Alloys .................. 22
CROSS REFERENCES OF INTERNATIONAL DESIGNATIONS—
DECLARATION OF ACCORD (DOA) TO ISO ..................................................... 23
RECOMMENDATION TO THE DECLARATION OF ACCORD ............................ 24
Footnotes ........................................................................................................ 25
Appendix A—Use of Designations ................................................................... 26
Appendix B—Deactivation of Registered Alloys ............................................... 26
Appendix C—General Guidelines for Determining Compliance
with "Sale of Alloy" and "Commercial Quantity" for
Purposes of Registering Wrought Aluminum and
Wrought Aluminum Alloys ......................................................... 26
DECLARATION OF ACCORD .............................................................................. 27
i
FOREWORD
Listed herein are designations and chemical composition limits for wrought aluminum and
wrought aluminum alloys registered with The Aluminum Association. Numerical designations
are assigned in accordance with the Recommendation—International Designation System for
Wrought Aluminum and Wrought Aluminum Alloys, which is printed on pages 24 through 26.
Additions may be made in accordance with the rules outlined in the Declaration of Accord
printed on page 27, and alloys will be deleted when no longer in commercial use (see table of
inactive alloys).
Since the International Designation System for Wrought Aluminum and Wrought Aluminum
Alloys is based on USA's national standard "American National Standard Alloy and Temper
Designation System for Aluminum ANSI H35.1," the system limits introduction of experimental
alloy compositions to USA registrations. An experimental alloy registered by USA under this
system is indicated by the prefix "X" and is subject to the following rules:
1. A composition shall not be designated as experimental ("X") for more than five years.
2. The "X" is dropped when the alloy is no longer experimental.
3. An experimental composition that is inactivated shall retain the prefix "X" for the duration of
its inactive status. If reactivated, the "X" shall be removed.
Some of the registered alloys may be the subject of patent or patent applications, and
their listing herein is not to be construed in any way as the granting of a license under
such patent right.
A list of the organizations that are signatories to the Declaration of Accord on the
Recommendation is printed on pages ii-iii.
SIGNATORIES TO THE DECLARATION OF ACCORD
The following organizations are signatories to the Declaration of Accord on an International Alloy Designation System
for Wrought Aluminum and Wrought Aluminum Alloys which is printed on page 27 of this publication.
The Aluminum Association Inc. USA
900 19th Street, N.W.
Washington, D.C. 20006
USA
www.aluminum.org
All-Russian Institute of Aviation Materials (VIAM) RUSSIA
17 Radio Ulitza
105005 Moscow
RUSSIA
www.viam.ru
Aluminium Association of Canada CANADA
1010 Sherbrooke Street West, Suite 1600
Montreal, Quebec H3A2R7
CANADA
www.aac.aluminium.qc.ca
Aluminium Federation Limited UK
Broadway House, Calthorpe Road, Five Ways
Birmingham B15 1TN
UNITED KINGDOM
www.alfed.org.uk
Aluminium Federation of South Africa SOUTH AFRICA
P. O. Box 423
Isando, 1600
REPUBLIC OF SOUTH AFRICA
www.afsa.org.za
Aluminium – Verband Schweiz SWITZERLAND
Hallenstrasse 15
Postfach
CH-8024 Zurich
SWITZERLAND
www.alu.ch
Gesamtverband Der Aluminium- GERMANY
industrie e.V. (GDA)
Am Bonneshof 5
D-40474 Dusseldorf
GERMANY
www.aluinfo.de
Associacao Brasileira Do Aluminio—ABAL BRAZIL
Rua Humberto 1, No. 220-4 Andar
Vila Mariana 04018-030
Sao Paulo-SP
BRAZIL
www.abal.org.br
The European Association of Aerospace A.E.C.M.A.
Industries—Standardization
Gulledelle 96
B-1200 Bruxelles
BELGIUM
www.aecma.org
Assomet Associazione Nazionale ITALY
Industrie Metalli Non Ferrosi
Centro Direzionale Ambrosizno—Pal. A/1
Via Dei Missaglia, 97
20142 Milano
ITALY
www.assomet.it
Austrian Non-Ferrous Metals Federation AUSTRIA
Wiedner Hauptstrasse 63
Postfach 338
A-1045 Wien IV
AUSTRIA
Australian Aluminium Council Limited AUSTRALIA
Level 1, Dickson Square
P. O. Box 63
Dickson, ACT 2602
AUSTRALIA
www.aluminium.org.au
Aluminium Center Belgium BELGIUM
Z.I. Research Park 310
1731 Zellik
BELGIUM
www.aluminiumcenter.be
Centro Nacional de Investigaciones SPAIN
Metalurgicas (CENIM)
Avda. Gregorio del Amo, 8
Ciudad Universitaria
28040 Madrid
SPAIN
www.cenim.csic.es
China Nonferrous Metals Techno-Economic CHINA
Research Institute
No. 9 Xizhang Hutong, Xizhimennei Street
Bejing, 100035
PEOPLES REPUBLIC OF CHINA
European Aluminium Association EAA
Avenue de Broqueville, 12
B-1150 Brussels
BELGIUM
www.aluminium.org
FEDEM FRANCE
Federation Des Minerais, Mineraux Industriels
Et Metaux Non Ferreux
17, rue Hamelin
75016 Paris
FRANCE
www.fedem.fr
ii
IRAM—Instituto Argentino De ARGENTINA
Normalizacion
Peru 556
C1068AAB
Buenos Aires
ARGENTINA
www.iram.org.ar
Instituto Mexicano del Alumino, A.C. MEXICO
Petarca 133-9 Piso
Col. Polanco
MEXICO, 11560, DF
www.imedal.com.mx
Institute of Non-Ferrous Metals POLAND
Light Metals Divison
32-050 Skawina
Ul. Pi Lsudskiego 19
POLAND
www.imn.gliwice.pl
Japan Aluminium Association JAPAN
Tsukamoto-Sozan Building
2-15, Ginza 4-Chome
Tokyo, Chuo-ku, 104-0061
JAPAN
www.aluminum.or.jp
S.C. Alprom S.A. ROMANIA
1 Milcov Street
23007 Slatina, Olt County
ROMANIA
Swedish Aluminium Association SWEDEN
P.O. Box 22307
SE-104 22
Stockholm
SWEDEN
www.svensktaluminium.com
VNMI – Association for the Dutch NETHERLANDS
Metallurgic Industry
P.O. Box 190
2700 AD Zoetermeer
NETHERLANDS
www.vnmi.nl
iii
Signatories (Continued)
CHEMICAL COMPOSITION LIMITS1,2
Only composition limits which are identical to those listed herein for a registered designation are applicable to that designation.
NATURAL IMPURITY LIMITS FOR WROUGHT UNALLOYED ALUMINUM
See footnotes on pages 13-14.
1
REGISTERED INTERNATIONAL DESIGNATION OTHERS39 ALUMINUM
No.75 DATE BY Si Fe Cu Mn Mg Cr Ni Zn Ti Ga V Each Total3 Minimum
1050 1954-07-01 USA 0.25 0.40 0.05 0.05 0.05 .... .... 0.05 0.03 .... 0.05 .... 0.03 .... 99.504
1050A 1972-09-22 EAA 0.25 0.40 0.05 0.05 0.05 .... .... 0.07 0.05 .... .... .... 0.03 .... 99.504
1060 1954-07-01 USA 0.25 0.35 0.05 0.03 0.03 .... .... 0.05 0.03 .... 0.05 .... 0.03 .... 99.604
1065 1973-08-22 USA 0.25 0.30 0.05 0.03 0.03 .... .... 0.05 0.03 .... 0.05 .... 0.03 .... 99.654
1070 1954-07-01 USA 0.20 0.25 0.04 0.03 0.03 .... .... 0.04 0.03 .... 0.05 .... 0.03 .... 99.704
1070A 1972-09-22 EAA 0.20 0.25 0.03 0.03 0.03 .... .... 0.07 0.03 .... .... .... 0.03 .... 99.704
1080 1954-07-01 USA 0.15 0.15 0.03 0.02 0.02 .... .... 0.03 0.03 0.03 0.05 .... 0.02 .... 99.804
++ 1080A 1972-09-22 EAA 0.15 0.15 0.03 0.02 0.02 .... .... 0.06 0.02 0.03 .... 6 0.02 .... 99.804
1085 1954-07-01 USA 0.10 0.12 0.03 0.02 0.02 .... .... 0.03 0.02 0.03 0.05 .... 0.01 .... 99.854
1090 1954-07-01 USA 0.07 0.07 0.02 0.01 0.01 .... .... 0.03 0.01 0.03 0.05 .... 0.01 .... 99.904
1098 1972-02-15 GERMANY 0.010 0.006 0.003 .... .... .... .... 0.015 0.003 .... .... .... 0.003 .... 99.985
REGISTERED COMPOSITIONS
REGISTERED INTERNATIONAL DESIGNATION OTHERS39 ALUMINUM
No.75 DATE BY Si Fe Cu Mn Mg Cr Ni Zn Ti Ga V Each Total3 Minimum
1100 1954-07-01 USA 0.95 Si + Fe 0.05-0.20 0.05 .... .... .... 0.10 .... .... .... 6 0.05 0.15 99.004
+ 1100A 2005-06-29 JAPAN 1.00 Si + Fe 0.05-0.20 0.05 0.10 .... .... 0.10 0.10 .... .... .... 0.05 0.15 99.004
1200 1966-09-23 USA 1.00 Si + Fe 0.05 0.05 .... .... .... 0.10 0.05 .... .... .... 0.05 0.15 99.004
1200A 1991-03-22 NORWAY 1.00 Si + Fe 0.10 0.30 0.30 0.10 .... 0.10 .... .... .... .... 0.05 0.15 99.004
130066 2000-12-13 FRANCE 0.20 0.30 0.05 0.03 0.03 ..... .... 0.20-0.50 0.03 .... .... .... 0.05 0.15 99.004
1110 1987-06-15 FRANCE 0.30 0.8 0.04 0.01 0.25 0.01 .... .... .... .... 0.02 B, 0.03 V+Ti 0.03 .... 99.104
1120 1982-07-07 AUSTRALIA 0.10 0.40 0.05-0.35 0.01 0.20 0.01 .... 0.05 .... 0.03 .... 0.05 B, 0.02 V+Ti 0.03 0.10 99.204
123066 1954-07-01 USA 0.70 Si + Fe 0.10 0.05 0.05 .... .... 0.10 0.03 .... 0.05 .... 0.03 .... 99.304
+ 1230A 2005-06-29 JAPAN 0.70 Si + Fe 0.10 0.05 0.05 .... .... 0.05 .... .... .... .... 0.03 .... 99.304
1235 1954-07-01 USA 0.65 Si + Fe 0.05 0.05 0.05 .... .... 0.10 0.06 .... 0.05 .... 0.03 .... 99.354
1435 1958-03-05 USA 0.15 0.30-0.50 0.02 0.05 0.05 .... .... 0.10 0.03 .... 0.05 .... 0.03 .... 99.354
1145 1954-07-01 USA 0.55 Si + Fe 0.05 0.05 0.05 .... .... 0.05 0.03 .... 0.05 .... 0.03 .... 99.454
1345 1956-10-08 USA 0.30 0.40 0.10 0.05 0.05 .... .... 0.05 0.03 .... 0.05 .... 0.03 .... 99.454
1445 1973-09-14 AUSTRALIA 0.50 Si + Fe20 0.0420 .... .... .... .... .... .... .... .... .... .... 0.05 99.454
1150 1973-08-02 AUSTRALIA 0.45 Si + Fe 0.05-0.20 0.05 0.05 .... .... 0.05 0.03 .... .... .... 0.03 .... 99.504
135018 1975-01-24 USA 0.10 0.40 0.05 0.01 .... 0.01 .... 0.05 .... 0.03 .... 0.05 B, 0.02 V+Ti 0.03 0.10 99.504
1350A 1979-02-15 GERMANY 0.25 0.40 0.02 .... 0.05 .... .... 0.05 .... .... .... 0.03 Cr+Mn+Ti+V 0.03 .... 99.504
++ 1450 1990-11-14 EAA 0.25 0.40 0.05 0.05 0.05 .... .... 0.07 0.10-0.20 .... .... 6 0.03 .... 99.504
CHEMICAL COMPOSITION LIMITS1,2
REGISTERED COMPOSITION--Continued
Only composition limits which are identical to those listed herein for a registered designation are applicable to that designation.
See footnotes on pages 13-14.
2
REGISTERED INTERNATIONAL DESIGNATION OTHERS39 ALUMINUM
No.75 DATE BY Si Fe Cu Mn Mg Cr Ni Zn Ti Ga V Each Total3 Minimum
1370 1976-04-20 FRANCE 0.10 0.25 0.02 0.01 0.02 0.01 .... 0.04 .... 0.03 .... 0.02 B, 0.02 V+Ti 0.02 0.10 99.704
1275 1986-03-24 SPAIN 0.08 0.12 0.05-0.10 0.02 0.02 .... .... 0.03 0.02 0.03 0.03 .... 0.01 .... 99.754
1185 1954-07-01 USA 0.15 Si + Fe 0.01 0.02 0.02 .... .... 0.03 0.02 0.03 0.05 .... 0.01 .... 99.854
1285 1954-07-01 USA 0.087 0.087 0.02 0.01 0.01 .... ... 0.03 0.02 0.03 0.05 .... 0.01 .... 99.854
1385 1987-06-15 FRANCE 0.05 0.12 0.02 0.01 0.02 0.01 .... 0.03 .... 0.03 .... 0.03 V+Ti40 0.01 .... 99.854
1188 1954-07-01 USA 0.06 0.06 0.005 0.01 0.01 .... .... 0.03 0.01 0.03 0.05 6 0.01 .... 99.884
1190 1987-06-15 FRANCE 0.05 0.07 0.01 0.01 0.01 0.01 .... 0.02 .... 0.02 .... 0.01 V+Ti41 0.01 .... 99.904
+ 1290 2005-06-29 JAPAN 0.050 0.030 0.050 .... .... .... .... .... .... .... .... .... 0.01 .... 99.905
1193 1964-09-29 USA 0.04 0.04 0.006 0.01 0.01 .... .... 0.03 0.01 0.03 0.05 .... 0.01 .... 99.934
1198 1990-10-04 FRANCE 0.010 0.006 0.006 0.006 .... .... .... 0.010 0.006 0.006 .... .... 0.003 .... 99.984
1199 1956-03-12 USA 0.006 0.006 0.006 0.002 0.006 .... .... 0.006 0.002 0.005 0.005 .... 0.002 .... 99.995
2001 1979-08-22 FRANCE 0.20 0.20 5.2-6.0 0.15-0.50 0.20-0.45 0.10 0.05 0.10 0.20 .... .... 0.05 Zr42 0.05 0.15 Remainder
2002 1975-08-25 FRANCE 0.35-0.8 0.30 1.5-2.5 0.20 0.50-1.0 0.20 .... 0.20 0.20 .... .... .... 0.05 0.15 Remainder
2004 1980-08-07 UK 0.20 0.20 5.5-6.5 0.10 0.50 .... .... 0.10 0.05 .... .... 0.30-0.50 Zr 0.05 0.15 Remainder
2005 1983-01-10 ARGENTINA 0.8 0.7 3.5-5.0 1.0 0.20-1.0 0.10 0.20 0.50 0.20 .... .... 0.20 Bi, 1.0-2.0 Pb 0.05 0.15 Remainder
2006 1983-01-10 ARGENTINA 0.8-1.3 0.7 1.0-2.0 0.6-1.0 0.50-1.4 .... 0.20 0.20 0.30 .... .... .... 0.05 0.15 Remainder
2007 1979-02-15 GERMANY 0.8 0.8 3.3-4.6 0.50-1.0 0.40-1.8 0.10 0.20 0.8 0.20 .... .... 26 0.10 0.30 Remainder
2007A 2001-02-21 ITALY 0.8 0.8 3.3-4.6 0.20-1.0 0.40-1.8 0.10 0.20 0.8 0.20 .... .... 68 0.10 0.30 Remainder
2008 1987-07-01 USA 0.50-0.8 0.40 0.7-1.1 0.30 0.25-0.50 0.10 .... 0.25 0.10 .... 0.05 .... 0.05 0.15 Remainder
2009 1990-01-24 USA 0.25 0.05 3.2-4.4 .... 1.0-1.6 .... .... 0.10 .... .... .... 44 0.05 0.15 Remainder
2010 1990-09-21 USA 0.50 0.50 0.7-1.3 0.10-0.40 0.40-1.0 0.15 .... 0.30 .... .... .... .... 0.05 0.15 Remainder
2011 1954-07-01 USA 0.40 0.7 5.0-6.0 .... .... .... .... 0.30 .... .... .... 8 0.05 0.15 Remainder
2011A 1982-02-11 SWITZERLAND 0.40 0.50 4.5-6.0 .... .... .... .... 0.30 .... .... .... 8 0.05 0.15 Remainder
2111 1993-07-07 USA 0.40 0.7 5.0-6.0 .... .... .... .... 0.30 .... .... .... 64 0.05 0.15 Remainder
2111A 2001-02-21 ITALY 0.40 0.7 5.0-6.0 0.15 0.15 .... .... 0.30 0.05 .... .... 69 0.05 0.15 Remainder
2111B 2001-09-05 SWITZERLAND 0.30 0.50 4.6-6.0 0.05 0.05 .... .... .... .... .... .... 70 0.05 0.15 Remainder
2012 1993-06-23 USA 0.40 0.7 4.0-5.5 .... .... .... .... 0.30 .... .... .... 63 0.05 0.15 Remainder
2013 2003-05-20 JAPAN 0.6-1.0 0.40 1.5-2.0 0.25 0.8-1.2 O.04-0.35 .... 0.25 0.15 .... .... .... 0.05 0.15 Remainder
2014 1954-07-01 USA 0.50-1.2 0.7 3.9-5.0 0.40-1.2 0.20-0.8 0.10 .... 0.25 0.15 .... .... 9 0.05 0.15 Remainder
2014A 1976-08-30 AECMA 0.50-0.9 0.50 3.9-5.0 0.40-1.2 0.20-0.8 0.10 0.10 0.25 0.15 .... .... 0.20 Zr+Ti 0.05 0.15 Remainder
2214 1954-07-01 USA 0.50-1.2 0.30 3.9-5.0 0.40-1.2 0.20-0.8 0.10 .... 0.25 0.15 .... .... 9 0.05 0.15 Remainder
2015 2003-06-24 SWITZERLAND 0.8 0.8 3.9-5.2 0.30-1.0 0.30-1.3 0.15 0.20 0.7 0.20 .... .... 71 0.05 0.15 Remainder
2016 2003-11-14 GERMANY 0.30-0.7 0.15 3.5-4.5 0.10-0.50 0.30-0.8 .... .... .... 0.05-0.15 .... .... 73 0.05 0.15 Remainder
2017 1954-07-01 USA 0.20-0.8 0.7 3.5-4.5 0.40-1.0 0.40-0.8 0.10 .... 0.25 0.15 .... .... 9 0.05 0.15 Remainder
2017A 1972-09-22 EAA 0.20-0.8 0.7 3.5-4.5 0.40-1.0 0.40-1.0 0.10 .... 0.25 .... .... .... 0.25 Zr+Ti 0.05 0.15 Remainder
2117 1954-07-01 USA 0.8 0.7 2.2-3.0 0.20 0.20-0.50 0.10 .... 0.25 .... .... .... .... 0.05 0.15 Remainder
2018 1954-07-01 USA 0.9 1.0 3.5-4.5 0.20 0.45-0.9 0.10 1.7-2.3 0.25 .... .... .... .... 0.05 0.15 Remainder
2218 1954-07-01 USA 0.9 1.0 3.5-4.5 0.20 1.2-1.8 0.10 1.7-2.3 0.25 .... .... .... .... 0.05 0.15 Remainder
2618 1954-07-01 USA 0.10-0.25 0.9-1.3 1.9-2.7 .... 1.3-1.8 .... 0.9-1.2 0.10 0.04-0.10 .... .... .... 0.05 0.15 Remainder
2618A 1972-09-22 EAA 0.15-0.25 0.9-1.4 1.8-2.7 0.25 1.2-1.8 .... 0.8-1.4 0.15 0.20 .... .... 0.25 Zr+Ti 0.05 0.15 Remainder
CHEMICAL COMPOSITION LIMITS1,2
REGISTERED COMPOSITION--Continued
Only composition limits which are identical to those listed herein for a registered designation are applicable to that designation.
See footnotes on pages 13-14.
3
REGISTERED INTERNATIONAL DESIGNATION OTHERS39 ALUMINUM
No.75 DATE BY Si Fe Cu Mn Mg Cr Ni Zn Ti Ga V Each Total3 Minimum
221910 1954-08-13 USA 0.20 0.30 5.8-6.8 0.20-0.40 0.02 .... .... 0.10 0.02-0.10 .... 0.05-0.15 0.10-0.25 Zr 0.05 0.15 Remainder
2319 1958-06-05 USA 0.20 0.30 5.8-6.8 0.20-0.40 0.02 .... .... 0.10 0.10-0.20 .... 0.05-0.15 0.10-0.25 Zr6 0.05 0.15 Remainder
2419 1972-10-12 USA 0.15 0.18 5.8-6.8 0.20-0.40 0.02 .... .... 0.10 0.02-0.10 .... 0.05-0.15 0.10-0.25 Zr 0.05 0.15 Remainder
2519 1985-02-07 USA 0.2528 0.3028 5.3-6.4 0.10-0.50 0.05-0.40 .... .... 0.10 0.02-0.10 .... 0.05-0.15 0.10-0.25 Zr 0.05 0.15 Remainder
2021 1981-05-28 UK 0.20 0.30 5.8-6.8 0.20-0.40 0.02 .... .... 0.10 0.02-0.10 .... 0.05-0.15 0.10-0.25 Zr29 0.05 0.15 Remainder
+ 2022 2004-08-17 FRANCE 0.15 0.20 4.5-5.5 0.15-0.50 0.10-0.45 0.05 … 0.05-0.30 0.15 … … … 0.05 0.15 Remainder
+ 2023 2004-08-17 FRANCE 0.10 0.15 3.6-4.5 0.30 1.0-1.6 0.10 … … 0.05 … … 0.05-0.15 Zr58 0.05 0.15 Remainder
2024 1954-07-01 USA 0.50 0.50 3.8-4.9 0.30-0.9 1.2-1.8 0.10 .... 0.25 0.15 .... .... 9 0.05 0.15 Remainder
2024A 1996-02-14 FRANCE 0.15 0.20 3.7-4.5 0.15-0.8 1.2-1.5 0.10 .... 0.25 0.15 .... .... .... 0.05 0.15 Remainder
2124 1970-10-02 USA 0.20 0.30 3.8-4.9 0.30-0.9 1.2-1.8 0.10 .... 0.25 0.15 .... .... 9 0.05 0.15 Remainder
2224 1978-05-04 USA 0.12 0.15 3.8-4.4 0.30-0.9 1.2-1.8 0.10 .... 0.25 0.15 .... .... .... 0.05 0.15 Remainder
2224A 1997-10-10 RUSSIA 0.10 0.15 3.8-4.5 0.40-0.8 1.2-1.6 .... 0.05 0.10 0.01-0.07 .... .... .... 0.05 0.15 Remainder
2324 1978-05-04 USA 0.10 0.12 3.8-4.4 0.30-0.9 1.2-1.8 0.10 .... 0.25 0.15 .... .... .... 0.05 0.15 Remainder
2424 1994-01-28 USA 0.10 0.12 3.8-4.4 0.30-0.6 1.2-1.6 .... .... 0.20 0.10 .... .... .... 0.05 0.15 Remainder
2524 1995-11-20 USA 0.06 0.12 4.0-4.5 0.45-0.7 1.2-1.6 0.05 .... 0.15 0.10 .... .... .... 0.05 0.15 Remainder
2025 1954-07-01 USA 0.50-1.2 1.0 3.9-5.0 0.40-1.2 0.05 0.10 .... 0.25 0.15 .... .... .... 0.05 0.15 Remainder
2026 1999-05-24 USA 0.05 0.07 3.6-4.3 0.30-0.8 1.0-1.6 .... .... 0.10 0.06 .... .... 0.05-0.25 Zr 0.05 0.15 Remainder
2027 2001-12-19 FRANCE 0.12 0.15 3.9-4.9 0.50-1.2 1.0-1.5 .... .... 0.20 0.08 .... .... 0.05-0.15 Zr 0.05 0.15 Remainder
+ 2028 2005-07-08 GERMANY 0.8 0.8 3.3-4.6 0.50-1.0 0.40-1.8 0.10 0.20 0.8 0.20 … … 76 0.10 0.30 Remainder
2030 1972-09-22 EAA 0.8 0.7 3.
本文档为【国际注册铝合金牌号及化学成分】,请使用软件OFFICE或WPS软件打开。作品中的文字与图均可以修改和编辑,
图片更改请在作品中右键图片并更换,文字修改请直接点击文字进行修改,也可以新增和删除文档中的内容。
该文档来自用户分享,如有侵权行为请发邮件ishare@vip.sina.com联系网站客服,我们会及时删除。
[版权声明] 本站所有资料为用户分享产生,若发现您的权利被侵害,请联系客服邮件isharekefu@iask.cn,我们尽快处理。
本作品所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用。
网站提供的党政主题相关内容(国旗、国徽、党徽..)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。